Pulsed magnetic field is generated when imposing pulse signal on high-frequency magnetic field. Distribution of the inner magnetic intensity in induction coils tends to be uniform. Furthermore oscillation and disturbance phenomena appear in the melt. In. situ Al2O3 and Al3Zr particulate reinforced aluminum matrix composites have been synthesized by direct melt reaction using AlZr（CO3）2 components under a foreign field. The size of reinforced particulates is 2-3 μm. They are well distributed in the matrix. Thermodynamic and kinetic analysis show that high-frequency pulsed magnetic field accelerates heat and mass transfer processes and improves the kinetic condition of in-situ fabrication.
Guirong Li Yutao Zhao Qixun Dai Hongjie Zhang Hongming Wang
To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of ωCaO：ωCaF2=2 ： 1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.
WANG Hong-mingLI Gui-rongDING Zhen-taoDAI Qi-xunLI Bo